Polymaker Fiberon PA612 CF Black
1.020.000 ₫
12 in stock
Fiberon PA612-CF Black is a carbon fiber-reinforced 3D printing filament engineered to provide superior mechanical strength and better moisture resistance compared to conventional PA6 nylon types. Thanks to its Warp-Free™ technology, it helps improve the dimensional stability of prints, reducing warping.
| Parameter name | Value |
|---|---|
|
Tensile Strength (X-Y)
|
91.9 ± 2.0 MPa |
|
Tensile Strength (Z)
|
48.3 ± 3.9 MPa |
|
Young’s modulus (X – Y)
|
5136.7 ± 192.2 MPa |
|
Young’s modulus (Z)
|
2786.4 ± 78.4 MPa |
|
Elongation at break (X – Y)
|
2.6 ± 0.2 % |
|
Elongation at break (Z)
|
2.1 ± 0.2 % |
|
Flexural modulus (X – Y)
|
4583.5 ± 62.7 MPa |
|
Flexural modulus (Z)
|
2264.8 ± 203.8 MPa |
|
Flexural strength (X – Y)
|
138.0 ± 2.2 MPa |
|
Flexural strength (Z)
|
73.5 ± 3.9 MPa |
|
Charpy impact strength (X-Y)
|
8.1 ± 0.8 kJ/m2 |
|
Charpy impact strength (Z)
|
N/A |
|
Density
|
1.03 g/cm3 at 23°C |
|
Melt index
|
9.9 g/10min |
|
Light transmission
|
N/A |
|
Flame retardancy
|
HB |